Title: Inclined stress corrosion cracks in steel pipelines
Author: Gamboa, E.
Citation: Corrosion Engineering Science and Technology, 2015; 50(3):191-195
Publisher: Maney Publishing
Issue Date: 2015
ISSN: 1478-422X
1743-2782
Statement of
Responsibility: 
E. Gamboa
Abstract: Stress corrosion cracking (SCC) in steel gas pipelines has been experienced in many regions of the world and have been known to cause ruptures. A typical description of a high pH SCC crack is a hoop aligned crack that grows directly into the pipe wall, perpendicular to the direction of applied stress. Many studies have been carried out to understand the crack growth rates of such cracks, and SCC management models have been developed to aid asset owners to manage SCC. However, a few cases have been found in Canada and Australia where high pH SCC cracks grow at an angle away from the perpendicular, causing the cracks to travel in the hoop direction subsurface. There is little knowledge as to how common this phenomenon occurs in the world, what causes it and whether current SCC management models can still be used for these inclined cracks. This paper presents the results of some studies carried out in order to better understand the occurrence and characteristics of this phenomenon.
Keywords: Stress corrosion cracking; Pipeline steel; Inclined cracks; Crack interaction; Microstructural texture
Description: Published online: 10 Feb 2015
Rights: © 2015 Institute of Materials, Minerals and Mining Published by Maney on behalf of the Institute.
DOI: 10.1179/1743278215Y.0000000006
Appears in Collections:Aurora harvest 7
Mechanical Engineering publications

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.