Title: In vitro wear rates of materials under different loads and varying pH
Author: Shabanian, M.
Richards, L.
Citation: Journal of Prosthetic Dentistry, 2002; 87(6):650-656
Publisher: Mosby Inc
Issue Date: 2002
ISSN: 0022-3913
1097-6841
Statement of
Responsibility: 
Mitra Shabanian and Lindsay C. Richards
Abstract: <h4>Statement of problem</h4>Despite the need for information about the wear characteristics of restorative materials, there have been few systemic studies of the factors that influence the rate of material wear.<h4>Purpose</h4>This study compared the wear rates of enamel and 3 tooth-colored restorative materials under different loads (0, 3.2, 6.7, and 9.95 kg) and pH levels (1.2, 3.3, and 7.0).<h4>Material and methods</h4>An electromechanical tooth wear machine was used so that standard restorations representing 3 materials could be worn by opposing enamel under controlled conditions. The wear rates of enamel, composite (Z100), a conventional glass ionomer cement (Fuji IX), and a resin-modified glass ionomer cement (Fuji II LC) were compared at a range of loads (0 to 9.95 kg) and pH levels (1.2 to 7.0) and also at different sites across each restoration. Ten specimens were randomly assigned to each experimental group. Wear assessment was performed with a modified light microscope to quantify the height changes at defined points across wear facets. Four-way analysis of variance was used to compare wear rates among materials, pH levels, loads, and sites. Post-hoc t tests identified significant differences between specific pairs of experimental conditions (P<.05).<h4>Results</h4>The wear rates of enamel and the other test materials varied significantly with pH (P<.0001), load (P<.0001), and type of material (P<.0001). Enamel wear was influenced most by varied pH, whereas the composite was least affected by acid. The conventional glass ionomer cement was more susceptible than the composite to the effects of varied pH; the acid susceptibility of the resin-modified glass ionomer cement was generally between that of the composite and conventional glass ionomer cement. Enamel and the conventional glass ionomer cement were affected similarly by load. The composite was more resistant than the conventional glass ionomer cement to wear at higher loads; the resin-modified glass ionomer cement exhibited intermediate load resistance.<h4>Conclusion</h4>Within the limitations of this study, the 3 test materials were more resistant than enamel to acid, with the composite demonstrating the lowest susceptibility to acid. The acid- and load-resistance of the resin-modified glass ionomer cement was consistently less than that of the composite and greater than that of the conventional glass ionomer cement.
Keywords: Dental Enamel; Humans; Tooth Attrition; Hydrochloric Acid; Zirconium; Water; Silicon Dioxide; Acetates; Resins, Synthetic; Composite Resins; Resin Cements; Dental Materials; Glass Ionomer Cements; Microscopy, Electron, Scanning; Analysis of Variance; Matched-Pair Analysis; Materials Testing; Dental Restoration, Permanent; Dental Restoration Wear; Hydrogen-Ion Concentration; Surface Properties; Stress, Mechanical; Weight-Bearing; Statistics as Topic
RMID: 0020020503
DOI: 10.1067/mpr.2002.125609
Description (link): http://www.elsevier.com/wps/find/journaldescription.cws_home/623237/description#description
Appears in Collections:Dentistry publications

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.