A CO₂-stable K₂NiF₄-type oxide (Nd ₀.₉La₀.₁)₂(Ni₀.₇₄Cu 0.₂₁Al₀.₀₅)O₄+δ for oxygen separation
Date
2013
Authors
Chen, Y.
Liao, Q.
Wei, Y.
Li, Z.
Wang, H.
Editors
Advisors
Journal Title
Journal ISSN
Volume Title
Type:
Journal article
Citation
Industrial and Engineering Chemistry Research, 2013; 52(25):8571-8578
Statement of Responsibility
Yan Chen, Qing Liao, Yanying Wei, Zhong Li and Haihui Wang
Conference Name
Abstract
A K2NiF4-type oxide (Nd0.9La0.1)2(Ni0.74Cu0.21Al0.05)O4+δ (NLNCA) has been successfully synthesized by a sol–gel method. The oxygen permeation and stability of the NLNCA membrane under CO2 atmosphere were systematically studied. A steady oxygen permeation flux of 0.39 mL/(min·cm2) was obtained through the NLNCA membrane with a membrane thickness of 0.6 mm at 975 °C when CO2 was used as the sweep gas. More importantly, the oxygen permeation flux has no significant decrease during 250 h operation, which indicates that the NLNCA membrane is stable under CO2. X-ray diffraction analysis of the spent membrane shows that the membrane retains K2NiF4-type structure and no carbonate was formed even exposed to CO2 after 250 h operation. The results indicate that the NLNCA membrane has a great potential application in supplying oxygen for oxyfuel combustion with CO2 capture. Moreover, the cost of the NLNCA is low, and it is beneficial for industrial application.
School/Discipline
Dissertation Note
Provenance
Description
Access Status
Rights
Copyright © 2013 American Chemical Society