2D modelling of inclined intergranular stress corrosion crack paths
Date
2017
Authors
Griggs, J.
Gamboa, E.
Lavigne, O.
Editors
Advisors
Journal Title
Journal ISSN
Volume Title
Type:
Journal article
Citation
Fatigue and Fracture of Engineering Materials and Structures, 2017; 40(4):543-555
Statement of Responsibility
J Griggs, E Gamboa and O Lavigne
Conference Name
Abstract
Inclined high pH stress corrosion cracking (SCC) is a type of intergranular environmen- tal cracking in gas pipelines, which differs from typical SCC by propagating at an angle from the wall direction. Investigations of Australian and Canadian inclined SCC colonies have not provided a clear indicator of a cause for the abnormal crack growth direction. This paper addresses the possibility of crack tip strain enhanced electrochemistry causing the inclination. Potentiodynamic tests were conducted to quantify the influence of strain on the electrochemistry, and strain was found to increase current density up to 300% in the SCC region. A model was developed that incorporates crack tip strain driven SCC growth, which showed good agreement with field grown cracks, and the aspect ratio of the grains was shown to have an effect on the inclination angle. The result s indicate that crack tip strain enhanced electrochemistry is a plausible cause for inclined SCC.
School/Discipline
Dissertation Note
Provenance
Description
Access Status
Rights
© 2016 Wiley Publishing Ltd.