Control of the damage resistance of nanocomposite TiSiN coatings on steels: Roles of residual stress
Date
2011
Authors
Ahmed, M.
Zhou, Z.
Munroe, P.
Li, L.
Xie, Z.
Editors
Advisors
Journal Title
Journal ISSN
Volume Title
Type:
Journal article
Citation
Thin Solid Films, 2011; 519(15):5007-5012
Statement of Responsibility
Mohammad Shoeb Ahmed, Zhi-feng Zhou, Paul Munroe, Lawrence Kwok Yan Li, Zonghan Xie
Conference Name
Abstract
Thermal annealing has often been used to reduce residual stress and improve mechanical properties and performance of hard coatings. In this work, nanocomposite TiSiN coatings were engineered onto steel substrates by reactive unbalanced magnetron sputtering. Following deposition, thermal annealing was performed at temperatures up to 900 °C. A marked decrease in residual stress was observed in the coatings with the increase of thermal annealing temperature. To ascertain the role of residual stress in the response of the coatings to contact damage, nanoindentation was used to probe the damage resistance of the coatings and Rockwell-C test used to evaluate their adhesion strength, as a function of thermal annealing temperature. A combination of high damage resistance and good adhesion strength was observed for the coating annealed at an intermediate temperature of 600 °C. © 2011 Elsevier B.V. All rights reserved.
School/Discipline
Dissertation Note
Provenance
Description
Access Status
Rights
Copyright © 2011 Elsevier B.V. All rights reserved.