Description and unique crystal-structure of waterhouseite, a new hydroxy manganese phosphate species from the Iron Monarch deposit, middleback ranges, South Australia
Date
2005
Authors
Pring, A.
Kolitsch, U.
Birch, W.
Editors
Advisors
Journal Title
Journal ISSN
Volume Title
Type:
Journal article
Citation
Canadian Mineralogist, 2005; 43(4):1401-1410
Statement of Responsibility
Conference Name
Abstract
Waterhouseite from the Iron Monarch mine, Iron Knob, South Australia, is a new hydroxy manganese phosphate species that has a unique crystal-structure. The mineral was found in a carbonate-rich zone with gatehouseite, seamanite, rhodochrosite, shigaite, barite, hausmannite and hematite. It occurs as divergent sprays of orange-brown to dark brown bladed crystals up to 1 mm in length but only up to 20 μm in thickness. The crystals are transparent with a pearly luster on cleavages, but it is vitreous to pearly on the tabular faces. The mineral is brittle, with a conchoidal fracture and a yellowish brown streak. There is a perfect cleavage on (100) and a probable cleavage on (001). The crystals show the principal forms {100} (dominant), {010}, {011} and {001}. All crystals are twinned on (100) by non-merohedry. The Mohs hardness is estimated to be ∼4, and the measured density is 3.55(5) g/cm<sup>3</sup> (calculated density is 3.591 g/cm<sup>3</sup>). Crystals are biaxial negative and length-slow, with α 1.730(3), β ∼1.738 and γ 1.738(4), but 2V could not be measured. Interference colors are normal, implying the absence of optical dispersion. The optical orientation is XYZ = bac (pseudo-orthorhombic), and the pleochroism is X pale brownish, Y brown-yellow, Z pale brownish, with absorption Z = X > Y. Electron-microprobe analyses yielded the empirical formula Mn<inf>7.29</inf>[(P<inf>1.81</inf>As<inf>0.07</inf> V<inf>0.04</inf>)<inf>∑1.92</inf>O<inf>7.68</inf>](OH,O) <inf>8.32</inf>, calculated on the basis of 16 O atoms. The simplified formula is Mn<inf>7</inf>(PO<inf>4</inf>)<inf>2</inf>(OH)<inf>8</inf>, in agreement with the crystal-structure determination. The strongest five lines in the powder X-ray-diffraction pattern [d in Å(I)(hkl)] are: 4.436(70)(111), 3.621(100)(202), 3.069 (50)(311), 2.941(40)(013), and 2.780(35)(020). Unit-cell parameters refined from powder-diffraction data, a 11.364(6), b 5.570(2), c 10.455(3) Å, β 96.61(3)°, V 657.4(2) Å <sup>3</sup> (Z = 2), agree very well with those refined from the single-crystal data. The crystal structure was solved by direct methods and refined in space group P2<inf>1</inf>/c to R1(F) = 5.15% and wR2<inf>all</inf>(F<sup>2</sup>) = 16.28% using data from a twinned crystal (by non-merohedry) with 1400 "observed" reflections with F<inf>o</inf>. > 4o-(F<inf>o</inf>). The crystal structure is characterized by a dense, complex framework of Mn(O,OH)<inf>6</inf> octahedra and PO<inf>4</inf> tetrahedra, which are linked by both edges and comers. Two different subunits can be recognized in the structure: arsenoclasite-type strips of edge-sharing octahedra (fragments of brucite-pyrochroite-type sheets of octahedra) and finite chains of edge-sharing octahedra (fragments of infinite rutile-type chains). The PO<inf>4</inf> tetrahedra provide a connection between the strips and the chains. Single-crystal Raman spectra confirm weak hydrogen bonding. A unique feature of the structure is that the single PO<inf>4</inf> tetrahedron shares two of its edges with Mn(O,OH)<inf>6</inf> octahedra. Only two synthetic anhydrous metal arsenates are known that show a corresponding sharing of two edges. The structure of waterhouseite has no equivalent, although the unit-cell parameters reveal some relations with the two chemical analogues allactite, Mn<inf>7</inf>(AsO<inf>4</inf>)<inf>2</inf>(OH)<inf>8</inf>, and raadeite, M9<inf>7</inf>(PO<inf>4</inf>)<inf>2</inf> (OH)<inf>8</inf>.